Hydroxypropyl methyl cellulose
1. Take the required amount of hot water into the container and heat to above 85., stir slowly and add the product gradually The cellulose initially floats on the water, but gradually disperses in water and forms homogeneous slurry. Goon stirring until it cools down and becomes clear
2. Another way is by heating the amount of 1/3 or 2/3 water to above 85℃, add the cellulose to obtain hot slurry, then add the remaining cold water and keep stirring, the mixture is obtained when the slurry cools to about 20 ℃
3. Cellulose's mesh is fine, and it 's in the presence of separate small particles in evenly stirred powder and can rapidly dissolve in water
4. Or add the cellulose slowly and evenly at room temperature and keep stirring until clear solution is obtained
Previous: How to improve the adhesion of putty
Next: Technical Data Sheet
Related News and Blogs
24
Aug., 2024
Let's meet Indonesia Coatings Exhibition 2024
The 10th Paintistanbul & Turkcoat Fair will be held at the Istanbul Exhibition Center in Turkey from May 8th...
19
Nov., 2021
What Causes A Cracked Putty Layer?
The one-off scraping thickness of the putty is directly proportional to the curing shrinkage strength, which increases in proportion to the tendency of the putty to crack.
04
Nov., 2021
Whether you are carrying out small repairs or building walls, knowing how to mix the mortar needs to be precise. If the mortar is too dry, the blocks will not stick together properly. If it is too wet, flowing mortar can spill out of the joints, resulting in wasted time and materials for clean-up.
25
Oct., 2021
The Effect of Winter Construction Temperature on Tile Adhesives
As we all know, tile adhesive is generally made from cement and mixed with various additives. It is mixed with water at the construction site and then applied to the wall or floor.
Get in Touch
Interested in how our HPMC can enhance your personal care formulations? Contact us to request a free sample and experience the superior quality of our cellulose ether products.